Synthesis of Hydroxyapatite using Precipitated Calcium Carbonate (PCC) from Limestones

Hydroxyapatite (HAp) is a material that widely applied in bone and teeth implant due to its biocompatibility and bioactivity. This material can be prepared from PCC by precipitation method using CaO and H₃PO₄ in ethanol. In this work, variations of phosphoric acid amount and aging time were investigated. The synthesized HAp was characterized by FT-IR, AAS, UV-Vis Spectrophotometer, PSA, SEM, and powder XRD. The results showed that the high concentration of calcium in PCC gives better yields in which PCC obtained from carbonation method has higher yield than that of caustic soda method. The determination of optimum phosphoric acid addition based on targeted Ca/P ratio (1.67) from HAp was obtained on the addition of 0.1271 mol phosphoric acid with Ca/P ratio of 1.66. The aging time gave significant effect to the particle size of synthesised HAp. The smallest particle size was obtained in aging time for 48 hours as high as 49.25 μm. FTIR spectra of the synthesized HAp show the presence of hydroxyl (-OH) group at 3438.8 cm^-1, PO₄ ^3- at 557.39 and 1035.7 cm^-1, and CaO at 1413.72 cm^-1. The synthesized HAp forms agglomeration solid based on the SEM analysis. The powder XRD data shows three highest peaks at 2θ i.e. 27.8296; 31.1037; and 34.3578 which corresponds to β-TCP (tricalcium phosphate) in accordance with JCPDS no.09-0169. The characteristic 2θ peak of hydroxyapatite with low intensity is observed from the synthesized HAp refer to the JCPDS data no. 09-0432.